FKM Terpolymer Pre-compound
|
vulcanizing system |
Grade Name |
Fluorine Content% |
Special Gravity g/cm3 |
Mooney Viscosity |
Hardness |
Tensile Strength |
Elongation at break |
Compression Set |
TR10 |
|
ML（1+
10, 121℃）
|
（Shore A） |
(MPa) | （%） |
200℃×24H*25%（%） |
(℃) |
||||
|
Bisphenol system |
FR3301 |
68 |
1.85 |
30±5 |
76 | 13 | 230 | 21 | -15 |
|
FR3303HF |
69.8 |
1.9 |
48±5 | 80 | 13 | 250 | 24 | -8 | |
| FR3313HF | 69.5 | 1.92 | 38±5 | 80 | 12 | 300 | 24 |
-8 |
|
|
FR3308G |
69 | 1.89 | 30±5 | 71 | 15 | 270 | 26 |
-8 |
|
| FR3314G | 69.5 | 1.92 | 33±5 | 64 | 13.5 | 290 | 26 |
-8 |
|
|
FR3361 |
68 | 1.85 | 30±5 | 75 | 11 | 230 | 21 | -15 | |
|
FR3402L |
66 | 1.83 | 40-45 | 75 | 13 | 240 | 17 | -19 | |
|
FR3461 |
68 | 1.85 | 40±5 | 75 | 14 | 240 | 21 | -15 | |
|
FR3502L |
67 | 1.83 | 50-55 | 75 | 12 | 200 | 20 | -20 | |
|
FR3501 |
68 |
1.85 |
50±5 |
77 | 13 | 210 | 21 | -15 | |
|
FR3561G |
69.5 |
1.89 |
50±4 |
77 | 13 | 210 | 23 | -7 | |
|
FR3561 |
68 |
1.86 |
50±5 |
75 | 14 | 240 | 21 |
-15 |
|
|
FR3661 |
68 |
1.85 |
60±5 |
77 | 14 | 210 | 21 |
-15 |
|
|
FR3663 |
68 |
1.86 |
60±5 |
77 |
14 |
230 | 21 |
-15 |
|
|
FR3701 |
68 |
1.85 |
70±5 |
78 |
14 |
200 | 20 |
-15 |
|
|
FR3761 |
68 |
1.85 |
70±5 |
75 |
14 |
200 | 20 |
-15 |
Remark:
(1) The test data is measured through professional inspectors,and as the technical specifications of our products. This can not be represented the test of products of different production processes by customers.
(2) Warning of mixing: FKM could not be mixed with metal powder or Amines; if mixing with Sulphur over 1% will hinder the vulcanization of FKM, it will cause the rubber to be completely unable to use.
(3) Warning of vulcanization:When FKM is vulcanizing at high temperature, it will produce trace HF toxic gas, ventilation is suggested during production.
(4) More information, please see our TDS.